| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 密度 | ASTM D-1505 | 0.948 | g/cm3 | |
| 表观密度 | ASTM D-1895 | 0.59-0.62 | g/cm3 | ||
| 熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 5 | g/10min | |
| 螺旋流动长度 | Internal Method | 203 | mm | ||
| 机械性能 | 拉伸模量 | 1% Secant | ASTM D-638 | 636 | MPa |
| 拉伸模量 | ASTM D-638 | 807 | MPa | ||
| 拉伸屈服强度 | ASTM D-638 | 24 | MPa | ||
| 拉伸断裂强度 | ASTM D-638 | 24.1 | MPa | ||
| 屈服伸长率 | ASTM D-638 | 12 | % | ||
| 断裂伸长率 | ASTM D-638 | 1500 | % | ||
| 弯曲模量 | 1% Secant | ASTM D-790 | 954 | MPa | |
| 弯曲模量 | 2% Secant | ASTM D-790 | 772 | MPa | |
| 弯曲模量 | ASTM D-790 | 1010 | MPa | ||
| 悬臂梁缺口冲击强度 | 23℃ | ASTM D-256 | 58.7 | J/m | |
| 悬臂梁冲击强度 | -18℃ | ASTM D-4812 | NO Break | ||
| 邵氏硬度 | ASTM D-2240 | 72 | |||
| 热性能 | 热变形温度 | 0.45MPa,未退火 | ASTM D-648 | 63.9 | ℃ |
| 脆化温度 | ASTM D-746 | ＜-76.1 | ℃ | ||
| 维卡软化点 | ASTM D-1525 | 125 | ℃ | ||
| 熔体温度 | ASTM D-3418 | 128 | ℃ | ||
| 结晶温度 | ASTM D-3418 | 113 | ℃ | ||