| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 熔体流动速率 | ASTM D-1238 | 6.0 | g/10min | |
| 密度 | ASTM D-1505 | 0.955 | g/cm3 | ||
| 机械性能 | 断裂点抗张强度(模片) | ASTM D-638 | 290 | kg/cm2 | |
| 弹性系数(模片) | ASTM D-638 | 8400 | kg/cm2 | ||
| 肖氏硬度 | ASTM D-2240 | 68 | |||
| 弯曲刚性 | ASTM D-747 | 9200 | kg/cm2 | ||
| 抗冲击强度 | ASTM D-256 | 11 | kg-cm/cm | ||
| 扭转刚性 | ASTM D-1043 | 10000 | kg/cm2 | ||
| 降伏点抗张强度(模片) | ASTM D-638 | 250 | kg/cm2 | ||
| 伸长率(模片) | ASTM D-638 | 760 | ％ | ||
| 热性能 | 低温脆裂温度 | 50％ | ASTM D-746 | ＜-76 | ℃ |
| 熔点 | ASTM D-2117 | 129 | ℃ | ||
| 卫氏软化温度 | ASTM D-1525 | 125 | ℃ | ||