| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 熔体流动速率 | 230℃/3.8kg | ASTM D-1238 | 3.3 | g/10min |
| 物理性能 | 比重 | ASTM D-792 | 1.19 | g/cm3 | |
| 模具收缩率 | Flow,3.20mm | ASTM D-955 | 0.50-0.70 | % | |
| 机械性能 | 拉伸模量 | ASTM D-638 | 2070 | MPa | |
| 拉伸屈服强度 | ASTM D-638 | 37.8 | MPa | ||
| 拉伸断裂强度 | ASTM D-638 | 30.3 | MPa | ||
| 拉伸屈服伸长率 | ASTM D-638 | 2.4 | % | ||
| 拉伸断裂伸长率 | ASTM D-638 | 17 | % | ||
| 弯曲模量 | 50.0mm Span | ASTM D-790 | 2340 | MPa | |
| 弯曲屈服强度 | 50.0mm Span | ASTM D-790 | 67.6 | MPa | |
| IZOD缺口冲击强度 | 23℃ | ASTM D-256 | 214 | J/m | |
| 电气性能 | 体积电阻率 | IEC 60093 | >1.0E+14 | ohm.cm | |
| 介电强度 | 3.20mm,in Oil | IEC 60243-1 | 20.00 | KV/mm | |
| 热性能 | 热变形温度 | 0.45MPa，未退火，3.20mm | ASTM D-648 | 86.1 | ℃ |
| 热变形温度 | 1.80MPa，未退火，3.20mm | ASTM D-648 | 75.0 | ℃ | |
| 维卡软化温度 | ASTM D-1525 | 93.9 | ℃ | ||
| CLTE | Flow,-40TO40℃ | ASTM E-831 | 0.000090 | cm/cm/℃ | |
| CLTE | Transverse,-40TO40℃ | ASTM E-831 | 0.000092 | cm/cm/℃ | |
| 燃烧性 | 1.50mm | UL 94 | V-0 | ||
| 燃烧性 | 2.79mm | UL 94 | 5VA | ||