| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 熔体流动速率 | 220℃×10kg | ASTM D-1238 | 25 | g/10min |
| 比重 | ASTM D-792 | 1.20 | 23/23℃ | ||
| 熔体流动速率 | 200℃ 5kg | ASTM D-1238 | 2.3 | g/10min | |
| 机械性能 | 弯曲弹性率 | ASTM D-790 | 2.0×104 | kg/cm2 | |
| 引张强度 | ASTM D-638 | 370 | kg/cm2 | ||
| 弯曲强度 | ASTM D-790 | 8360 | lb/in2 | ||
| 弯曲弹性率 | ASTM D-790 | 2.8×105 | lb/in2 | ||
| IZOD冲击强度 | 1/4〃 | ASTM D-256 | 3.9 | ft.lb/in | |
| IZOD冲击强度 | 1/8" | ASTM D-256 | 23 | kg.cm/cm | |
| 引张强度 | ASTM D-638 | 5250 | lb/in2 | ||
| IZOD冲击强度 | 1/8" | ASTM D-256 | 4.3 | ft.lb/in | |
| 洛氏硬度 | ASTM D-785 | 95 | R | ||
| 伸长率 | ASTM D-638 | 30 | % | ||
| 弯曲强度 | ASTM D-790 | 590 | kg/cm2 | ||
| IZOD冲击强度 | 1/4〃 | ASTM D-256 | 21 | kg.cm/cm | |
| 热性能 | 热变形温度 | ASTM D-648 | 89(192) | ℃ | |
| 热变形温度 | ASTM D-648 | 81(178) | ℉ | ||
| 维卡软化点 | ASTM D-1525 | 98 | ℃ | ||
| 维卡软化点 | ASTM D-1525 | 214 | ℉ | ||
| 燃烧性 | File No. E56070 UL&C-UL | 1/16"V-O | |||